Sample: ZX30_10pct_TD200_TA350_15s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78865
EBSD (3)
Settings
Sample orientation vertical direction:
RD
Scan date:
5/28/24
Scan date:
1/16/24
Scan date:
3/9/25
SEM view field width:
550 µm
Scan Width:
400 µm
SEM view field width:
550 µm
Scan Height:
400 µm
Scan Width:
400 µm
Scan Height:
400 µm
Step size:
1 µm
Step size:
1 µm
frames per second:
80 fps
frames per second:
131 fps
frames per second:
100 fps
EBSD Camera Binning:
1 x 1
EBSD Camera Binning:
1 x 1
Background setting:
standard
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
1 µm diamond paste
Final Polishing Step:
fumed Si
Grid type:
hex
Voltage:
30 kV
Final Polishing Step:
fumed Si
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.89
% points with CI>0.1:
0.879
% points with CI>0.1:
0.88
Alloy:
ZX30
Unloaded strain:
11%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
55.5 %
Total Fraction Less than 1º:
31.6 %
Total Fraction Less than 1º:
60.3 %
Composition Ca content:
0.096 wt%
Number of grains:
575
Number of grains:
546
Number of grains:
565
Average Diameter:
16.8 µm
Average Diameter:
16 µm
Average Diameter:
16.5 µm
Twin fraction:
0.006
Files
Gleeble (1)
Settings
Test Date:
9/8/2023
Testing Mode:
PSC
Initial height or thickness:
9.95 mm
Initial width:
15.04 mm
Initial length:
20.09 mm
Final height or thickness:
8.87 mm
Final length:
20.54 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.1
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
350 ºC
Post-deformation Soak Time:
15 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.88
% points with CI>0.1:
0.879
% points with CI>0.1:
0.89
Alloy:
ZX30
Unloaded strain:
11%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
31.6 %
Total Fraction Less than 1º:
60.3 %
Total Fraction Less than 1º:
55.5 %
Composition Ca content:
0.096 wt%
Number of grains:
565
Number of grains:
575
Number of grains:
546
Average Diameter:
16.5 µm
Average Diameter:
16 µm
Average Diameter:
16.8 µm
Twin fraction:
0.006
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.88
% points with CI>0.1:
0.879
% points with CI>0.1:
0.89
Alloy:
ZX30
Unloaded strain:
11%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
31.6 %
Total Fraction Less than 1º:
55.5 %
Total Fraction Less than 1º:
60.3 %
Composition Ca content:
0.096 wt%
Number of grains:
575
Number of grains:
546
Number of grains:
565
Average Diameter:
16.8 µm
Average Diameter:
16 µm
Average Diameter:
16.5 µm
Twin fraction:
0.006