Sample: ZX30_10pct_TD200_TA350_270s
Ungroup ProcessesEBSD (1)
Settings
Scan date:
5/24/24
SEM view field width:
550
µm
Scan Width:
400
µm
Scan Height:
400
µm
Step size:
1
µm
frames per second:
66
fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
fumed Si
Voltage:
30
kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX30
Total Fraction Less than 1º:
53.2
%
Unloaded strain:
10%
Composition Zn content:
3.03
wt%
Number of grains:
195
Average Diameter:
27
µm
Composition Ca content:
0.096
wt%
Files
Gleeble (1)
Settings
Test Date:
5/8/24
Testing Mode:
PSC
Initial height or thickness:
9.97
mm
Initial width:
15.01
mm
Initial length:
19.98
mm
Final height or thickness:
8.96
mm
Final length:
20.64
mm
Pre-deformation soak Temp:
200
ºC
Deformations:
1
Initial Strain Rate:
0.5
/s
Strain Per pass:
0.1
Stage One - Temp during Deformations:
200
ºC
Post-deformation Soak Temp:
350
ºC
Post-deformation Soak Time:
270
s
Quench Duration:
45
s
Rate to Temp:
5
ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600
s
Specimen orientation:
CD || ED
Measurements
Alloy:
ZX30
Total Fraction Less than 1º:
53.2
%
Unloaded strain:
10%
Composition Zn content:
3.03
wt%
Number of grains:
195
Average Diameter:
27
µm
Composition Ca content:
0.096
wt%
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1
hr
Solution treatment Temp:
325
ºC
Measurements
Alloy:
ZX30
Total Fraction Less than 1º:
53.2
%
Unloaded strain:
10%
Composition Zn content:
3.03
wt%
Number of grains:
195
Average Diameter:
27
µm
Composition Ca content:
0.096
wt%