Sample: ZX30_10pct_TD200_TA350_60s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78868
EBSD (3)
Settings
Sample orientation vertical direction:
RD
Scan date:
5/20/24
Scan date:
5/13/24
Scan date:
3/7/25
SEM view field width:
550 µm
Scan Width:
400 µm
SEM view field width:
550 µm
Scan Height:
400 µm
Scan Width:
400 µm
Scan Height:
400 µm
Step size:
1 µm
Step size:
1 µm
frames per second:
66 fps
frames per second:
100 fps
EBSD Camera Binning:
1 x 1
EBSD Camera Binning:
1 x 1
Background setting:
standard
Background setting:
enhanced
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
fumed Si
Grid type:
hex
Voltage:
30 kV
Final Polishing Step:
fumed Si
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.92
% points with CI>0.1:
0.89
% points with CI>0.1:
0.8658
Alloy:
ZX30
Unloaded strain:
9%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
48.9 %
Total Fraction Less than 1º:
61.2 %
Total Fraction Less than 1º:
81 %
Composition Ca content:
0.096 wt%
Number of grains:
282
Number of grains:
279
Number of grains:
344
Average Diameter:
23 µm
Average Diameter:
24 µm
Average Diameter:
21.4 µm
Twin fraction:
0.006
Files
Gleeble (1)
Settings
Test Date:
4/26/24
Testing Mode:
PSC
Initial height or thickness:
9.97 mm
Initial width:
14.95 mm
Initial length:
19.96 mm
Final height or thickness:
9.06 mm
Final length:
20.57 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.1
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
350 ºC
Post-deformation Soak Time:
60 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.8658
% points with CI>0.1:
0.89
% points with CI>0.1:
0.92
Alloy:
ZX30
Unloaded strain:
9%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
61.2 %
Total Fraction Less than 1º:
81 %
Total Fraction Less than 1º:
48.9 %
Composition Ca content:
0.096 wt%
Number of grains:
344
Number of grains:
282
Number of grains:
279
Average Diameter:
21.4 µm
Average Diameter:
24 µm
Average Diameter:
23 µm
Twin fraction:
0.006
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.8658
% points with CI>0.1:
0.89
% points with CI>0.1:
0.92
Alloy:
ZX30
Unloaded strain:
9%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
61.2 %
Total Fraction Less than 1º:
48.9 %
Total Fraction Less than 1º:
81 %
Composition Ca content:
0.096 wt%
Number of grains:
282
Number of grains:
279
Number of grains:
344
Average Diameter:
23 µm
Average Diameter:
24 µm
Average Diameter:
21.4 µm
Twin fraction:
0.006