Sample: ZX30_5pct_TD200_TA350_15s_d03
Ungroup ProcessesEBSD (1)
Settings
Scan date:
1/17/24
SEM view field width:
530
µm
Scan Width:
400
µm
Scan Height:
395
µm
Step size:
1
µm
frames per second:
135
fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
1 µm diamond paste
Voltage:
30
kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.75
Alloy:
ZX30
Unloaded strain:
6%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
6.1
%
Composition Ca content:
0.096
wt%
Number of grains:
622
Average Diameter:
14.8
µm
Files
Gleeble (1)
Settings
Test Date:
9/8/2023
Testing Mode:
PSC
Initial height or thickness:
10.02
mm
Initial width:
15.01
mm
Initial length:
19.98
mm
Final height or thickness:
9.39
mm
Final length:
20.29
mm
Pre-deformation soak Temp:
200
ºC
Deformations:
1
Initial Strain Rate:
0.5
/s
Strain Per pass:
0.05
Stage One - Temp during Deformations:
200
ºC
Post-deformation Soak Temp:
350
ºC
Post-deformation Soak Time:
15
s
Quench Duration:
45
s
Rate to Temp:
5
ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600
s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.75
Alloy:
ZX30
Unloaded strain:
6%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
6.1
%
Composition Ca content:
0.096
wt%
Number of grains:
622
Average Diameter:
14.8
µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1
hr
Solution treatment Temp:
325
ºC
Measurements
% points with CI>0.1:
0.75
Alloy:
ZX30
Unloaded strain:
6%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
6.1
%
Composition Ca content:
0.096
wt%
Number of grains:
622
Average Diameter:
14.8
µm