Sample: ZX30_5pct_TD200_TA350_270s_d05

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78874
EBSD (2)
Settings
Sample orientation vertical direction:
RD
Scan date:
2/6/25
SEM view field width:
3100 µm
SEM view field width:
550 µm
Scan Width:
3000 µm
Scan Width:
400 µm
Scan Height:
100 µm
Scan Height:
400 µm
Step size:
5 µm
Step size:
1 µm
frames per second:
125 fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Grid type:
hex
Final Polishing Step:
fumed Si
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.929
% points with CI>0.1:
0.794
Alloy:
ZX30
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
74.6 %
Total Fraction Less than 1º:
73 %
Composition Ca content:
0.096 wt%
Number of grains:
184
Number of grains:
168
Average Diameter:
29.8 µm
Average Diameter:
41.8 µm
Files
Gleeble (1)
Settings
Test Date:
10/18/24
Testing Mode:
PSC
Initial height or thickness:
9.97 mm
Initial width:
14.96 mm
Initial length:
19.93 mm
Final height or thickness:
9.3 mm
Final length:
20.33 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.05
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
350 ºC
Post-deformation Soak Time:
270 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.794
% points with CI>0.1:
0.929
Alloy:
ZX30
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
74.6 %
Total Fraction Less than 1º:
73 %
Composition Ca content:
0.096 wt%
Number of grains:
184
Number of grains:
168
Average Diameter:
41.8 µm
Average Diameter:
29.8 µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.929
% points with CI>0.1:
0.794
Alloy:
ZX30
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
73 %
Total Fraction Less than 1º:
74.6 %
Composition Ca content:
0.096 wt%
Number of grains:
168
Number of grains:
184
Average Diameter:
41.8 µm
Average Diameter:
29.8 µm