Sample: ZX30_TD200_AS-DEF

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78877
EBSD (11)
Settings
Scan date:
1/25/24
Scan date:
9/12/22
Scan date:
1/18/23
Scan date:
1/22/24
Scan date:
2/8/24
Sample orientation vertical direction:
RD
Scan Width:
297 µm
Scan date:
8/12/24
SEM view field width:
100 µm
SEM view field width:
520 µm
Scan Width:
400 µm
Scan date:
8/16/24
Scan Width:
1500 µm
Scan Width:
1000 µm
Scan Width:
99 µm
SEM view field width:
550 µm
Scan Height:
200 µm
Scan Width:
27.5 µm
Scan Width:
514 µm
Scan Height:
400 µm
Scan Height:
300 µm
Scan Height:
500 µm
Scan Width:
400 µm
Scan Height:
75 µm
Scan Height:
27 µm
Step size:
0.15 µm
Step size:
5 µm
Scan Height:
389 µm
Scan Width:
300 µm
Step size:
1 µm
Step size:
3 µm
Scan Height:
250 µm
frames per second:
20 fps
frames per second:
60 fps
Scan Height:
400 µm
Step size:
0.2 µm
Step size:
0.15 µm
EBSD Camera Binning:
1 x 1
Step size:
0.15 µm
Step size:
1 µm
frames per second:
60 fps
frames per second:
40 fps
EBSD Camera Binning:
1 x 1
frames per second:
55 fps
Background setting:
standard
Final Polishing Step:
1 µm diamond paste
frames per second:
73 fps
Voltage:
30 kV
Background setting:
standard
Grid type:
square
EBSD Camera Binning:
1 x 1
Beam Intensity or current:
20
Background setting:
standard
Final Polishing Step:
1 µm diamond paste
Grid type:
hexagonal
Grid type:
square
CI>0.1 after rescan:
0.786
Final Polishing Step:
1 µm diamond paste
Grid type:
hexagonal
Grid type:
square
Voltage:
30 kV
CI>0.1 after rescan:
0.794
Final Polishing Step:
fumed Si
Voltage:
30 kV
Beam Intensity or current:
20
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.415
% points with CI>0.1:
0.515
% points with CI>0.1:
0.496
% points with CI>0.1:
0.616
% points with CI>0.1:
0.482
Average dislocation density:
1.3*10^14
Average dislocation density:
2.7*10^14
Average dislocation density:
2.1*10^14
Basal PF Max:
7.7 MRD
name on specimen mount:
ZX30C_lowT1pass_d02
Total Fraction Less than 1º:
1.2 %
Total Fraction Less than 1º:
0 %
Total Fraction Less than 1º:
0.4 %
Unloaded strain:
17%
Alloy:
ZX30
Number of grains:
705
Number of grains:
81
Average Diameter:
13.5 µm
Average Diameter:
20.7 µm
Composition Zn content:
3.03 wt%
Composition Ca content:
0.096 wt%
Twin fraction:
0.035
Twin fraction:
0.094
Files
Gleeble (1)
Settings
Test Date:
8/31/22
Test Mode:
PSC
Testing Mode:
PSC
Initial height or thickness:
10 mm
Final height or thickness:
8.31 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.415
% points with CI>0.1:
0.515
% points with CI>0.1:
0.496
% points with CI>0.1:
0.616
% points with CI>0.1:
0.482
Average dislocation density:
1.3*10^14
Average dislocation density:
2.7*10^14
Average dislocation density:
2.1*10^14
Basal PF Max:
7.7 MRD
name on specimen mount:
ZX30C_lowT1pass_d02
Total Fraction Less than 1º:
1.2 %
Total Fraction Less than 1º:
0 %
Total Fraction Less than 1º:
0.4 %
Unloaded strain:
17%
Alloy:
ZX30
Number of grains:
705
Number of grains:
81
Average Diameter:
13.5 µm
Average Diameter:
20.7 µm
Composition Zn content:
3.03 wt%
Composition Ca content:
0.096 wt%
Twin fraction:
0.035
Twin fraction:
0.094
Files
GND Calculation (3)
Measurements
% points with CI>0.1:
0.415
% points with CI>0.1:
0.515
% points with CI>0.1:
0.496
% points with CI>0.1:
0.616
% points with CI>0.1:
0.482
Average dislocation density:
1.3*10^14
Average dislocation density:
2.7*10^14
Average dislocation density:
2.1*10^14
Basal PF Max:
7.7 MRD
name on specimen mount:
ZX30C_lowT1pass_d02
Total Fraction Less than 1º:
1.2 %
Total Fraction Less than 1º:
0 %
Total Fraction Less than 1º:
0.4 %
Unloaded strain:
17%
Alloy:
ZX30
Number of grains:
705
Number of grains:
81
Average Diameter:
13.5 µm
Average Diameter:
20.7 µm
Composition Zn content:
3.03 wt%
Composition Ca content:
0.096 wt%
Twin fraction:
0.035
Twin fraction:
0.094
Files
Optical Microscopy (1)
Settings
Date:
2/10/2023
Measurements
% points with CI>0.1:
0.415
% points with CI>0.1:
0.515
% points with CI>0.1:
0.496
% points with CI>0.1:
0.616
% points with CI>0.1:
0.482
Average dislocation density:
1.3*10^14
Average dislocation density:
2.7*10^14
Average dislocation density:
2.1*10^14
Basal PF Max:
7.7 MRD
name on specimen mount:
ZX30C_lowT1pass_d02
Total Fraction Less than 1º:
1.2 %
Total Fraction Less than 1º:
0 %
Total Fraction Less than 1º:
0.4 %
Unloaded strain:
17%
Alloy:
ZX30
Number of grains:
705
Number of grains:
81
Average Diameter:
13.5 µm
Average Diameter:
20.7 µm
Composition Zn content:
3.03 wt%
Composition Ca content:
0.096 wt%
Twin fraction:
0.035
Twin fraction:
0.094
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.415
% points with CI>0.1:
0.515
% points with CI>0.1:
0.496
% points with CI>0.1:
0.616
% points with CI>0.1:
0.482
Average dislocation density:
1.3*10^14
Average dislocation density:
2.7*10^14
Average dislocation density:
2.1*10^14
Basal PF Max:
7.7 MRD
name on specimen mount:
ZX30C_lowT1pass_d02
Total Fraction Less than 1º:
1.2 %
Total Fraction Less than 1º:
0 %
Total Fraction Less than 1º:
0.4 %
Unloaded strain:
17%
Alloy:
ZX30
Number of grains:
705
Number of grains:
81
Average Diameter:
13.5 µm
Average Diameter:
20.7 µm
Composition Zn content:
3.03 wt%
Composition Ca content:
0.096 wt%
Twin fraction:
0.035
Twin fraction:
0.094
Files
Texture (1)
Settings
total area:
1.4 mm^2
Measurements
% points with CI>0.1:
0.415
% points with CI>0.1:
0.515
% points with CI>0.1:
0.496
% points with CI>0.1:
0.616
% points with CI>0.1:
0.482
Average dislocation density:
1.3*10^14
Average dislocation density:
2.7*10^14
Average dislocation density:
2.1*10^14
Basal PF Max:
7.7 MRD
name on specimen mount:
ZX30C_lowT1pass_d02
Total Fraction Less than 1º:
1.2 %
Total Fraction Less than 1º:
0 %
Total Fraction Less than 1º:
0.4 %
Unloaded strain:
17%
Alloy:
ZX30
Number of grains:
705
Number of grains:
81
Average Diameter:
13.5 µm
Average Diameter:
20.7 µm
Composition Zn content:
3.03 wt%
Composition Ca content:
0.096 wt%
Twin fraction:
0.035
Twin fraction:
0.094
Files