Sample: ZX30_TD200_TA275_135s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78878
EBSD (2)
Settings
Sample orientation vertical direction:
RD
Scan date:
3/15/24
Scan date:
3/13/25
SEM view field width:
550 µm
Scan Width:
400 µm
SEM view field width:
550 µm
Scan Height:
400 µm
Scan Width:
400 µm
Step size:
1 µm
Scan Height:
400 µm
Step size:
1 µm
frames per second:
60 fps
EBSD Camera Binning:
1 x 1
frames per second:
50 fps
Background setting:
standard
EBSD Camera Binning:
1 x 1
Grid type:
hexagonal
Background setting:
standard
Patterns Saved?:
yes
Grid type:
hex
Final Polishing Step:
1 µm diamond paste
Final Polishing Step:
fumed Si
Voltage:
30 kV
CI>0.1 after rescan:
0.768
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.677
% points with CI>0.1:
0.645
Alloy:
ZX30
Unloaded strain:
18%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
43 %
Total Fraction Less than 1º:
32.9 %
Composition Ca content:
0.096 wt%
Number of grains:
1610
Number of grains:
1542
Average Diameter:
10 µm
Average Diameter:
9.2 µm
Twin fraction:
0.01
Files
Gleeble (1)
Settings
Test Date:
3/11/24
Testing Mode:
PSC
Initial height or thickness:
9.97 mm
Initial width:
15.05 mm
Initial length:
19.98 mm
Final height or thickness:
8.21 mm
Final length:
21.13 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
275 ºC
Post-deformation Soak Time:
135 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.645
% points with CI>0.1:
0.677
Alloy:
ZX30
Unloaded strain:
18%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
43 %
Total Fraction Less than 1º:
32.9 %
Composition Ca content:
0.096 wt%
Number of grains:
1542
Number of grains:
1610
Average Diameter:
9.2 µm
Average Diameter:
10 µm
Twin fraction:
0.01
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.677
% points with CI>0.1:
0.645
Alloy:
ZX30
Unloaded strain:
18%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
43 %
Total Fraction Less than 1º:
32.9 %
Composition Ca content:
0.096 wt%
Number of grains:
1610
Number of grains:
1542
Average Diameter:
9.2 µm
Average Diameter:
10 µm
Twin fraction:
0.01
Files