Sample: ZX30_TD200_TA275_2500s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78880
EBSD (2)
Settings
Scan date:
5/7/24
Scan date:
3/29/24
SEM view field width:
550 µm
Scan Width:
400 µm
Scan Height:
400 µm
Step size:
1 µm
frames per second:
150 fps
frames per second:
66 fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Background setting:
enhanced
Grid type:
hexagonal
Final Polishing Step:
1 µm diamond paste
Final Polishing Step:
fumed Si
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.836
% points with CI>0.1:
0.757
Alloy:
ZX30
Unloaded strain:
15%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
62.8 %
Total Fraction Less than 1º:
72.2 %
Composition Ca content:
0.096 wt%
Number of grains:
1004
Number of grains:
1137
Average Diameter:
12 µm
Files
Gleeble (1)
Settings
Test Date:
3/25/24
Testing Mode:
PSC
Initial height or thickness:
9.97 mm
Initial width:
14.98 mm
Initial length:
19.98 mm
Final height or thickness:
8.44 mm
Final length:
20.94 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.836
% points with CI>0.1:
0.757
Alloy:
ZX30
Unloaded strain:
15%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
62.8 %
Total Fraction Less than 1º:
72.2 %
Composition Ca content:
0.096 wt%
Number of grains:
1004
Number of grains:
1137
Average Diameter:
12 µm
Files
Heat Treatment (1)
Settings
Date:
3/26/24
Who did the treatment:
Tracy Berman
Furnace:
Thermolyne
Target Temperature:
275 ºC
Furance Set Point:
272 ºC
Time in furnace:
60 minutes
Time at temp with 5 deg:
45 minutes
Time above 200ºC:
56 minutes
Quench:
water
Measurements
% points with CI>0.1:
0.757
% points with CI>0.1:
0.836
Alloy:
ZX30
Unloaded strain:
15%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
62.8 %
Total Fraction Less than 1º:
72.2 %
Composition Ca content:
0.096 wt%
Number of grains:
1004
Number of grains:
1137
Average Diameter:
12 µm
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.757
% points with CI>0.1:
0.836
Alloy:
ZX30
Unloaded strain:
15%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
72.2 %
Total Fraction Less than 1º:
62.8 %
Composition Ca content:
0.096 wt%
Number of grains:
1137
Number of grains:
1004
Average Diameter:
12 µm
Files