Sample: ZX30_TD200_TA275_585s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78883
EBSD (4)
Settings
Scan date:
5/6/24
Scan date:
3/19/24
Scan date:
2/28/24
SEM view field width:
1150 µm
SEM view field width:
550 µm
Scan Width:
400 µm
Scan Width:
542 µm
Scan Width:
800 µm
Scan Height:
800 µm
Scan Height:
400 µm
Scan Height:
410 µm
Step size:
1.5 µm
Step size:
1 µm
frames per second:
150 fps
frames per second:
110 fps
frames per second:
66 fps
EBSD Camera Binning:
1 x 1
Background setting:
enhanced
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
fumed Si
Final Polishing Step:
1 µm diamond paste
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.782
% points with CI>0.1:
0.746
Alloy:
ZX30
Total Fraction Less than 1º:
47.4 %
Total Fraction Less than 1º:
57.6 %
Unloaded strain:
17%
Composition Zn content:
3.03 wt%
Number of grains:
1585
Number of grains:
4119
Total Fraction Less than 1º:
60.3 %
Total Fraction Less than 1º:
72.4 %
Average Diameter:
11 µm
Average Diameter:
12 µm
Composition Ca content:
0.096 wt%
Number of grains:
1408
Number of grains:
1308
Average Diameter:
11 µm
Files
Gleeble (1)
Settings
Test Date:
2/20/24
Testing Mode:
PSC
Initial height or thickness:
9.98 mm
Initial width:
14.97 mm
Initial length:
20.02 mm
Final height or thickness:
8.24 mm
Final length:
21.08 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.05
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
275 ºC
Post-deformation Soak Time:
585 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.746
% points with CI>0.1:
0.782
Alloy:
ZX30
Total Fraction Less than 1º:
57.6 %
Total Fraction Less than 1º:
47.4 %
Unloaded strain:
17%
Composition Zn content:
3.03 wt%
Number of grains:
4119
Number of grains:
1585
Total Fraction Less than 1º:
72.4 %
Total Fraction Less than 1º:
60.3 %
Average Diameter:
11 µm
Average Diameter:
12 µm
Composition Ca content:
0.096 wt%
Number of grains:
1308
Number of grains:
1408
Average Diameter:
11 µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.746
% points with CI>0.1:
0.782
Alloy:
ZX30
Total Fraction Less than 1º:
57.6 %
Total Fraction Less than 1º:
47.4 %
Unloaded strain:
17%
Composition Zn content:
3.03 wt%
Number of grains:
1585
Number of grains:
4119
Total Fraction Less than 1º:
72.4 %
Total Fraction Less than 1º:
60.3 %
Average Diameter:
12 µm
Average Diameter:
11 µm
Composition Ca content:
0.096 wt%
Number of grains:
1408
Number of grains:
1308
Average Diameter:
11 µm
Files