Sample: ZX30_TD200_TA275_6h

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78884
EBSD (5)
Settings
Scan date:
5/7/24
Scan date:
4/26/24
Scan date:
4/17/24
Scan date:
4/16/24
SEM view field width:
550 µm
Scan Width:
400 µm
Scan Height:
400 µm
Step size:
1 µm
frames per second:
100 fps
frames per second:
198 fps
frames per second:
66 fps
frames per second:
150 fps
frames per second:
129 fps
EBSD Camera Binning:
1 x 1
Background setting:
enhanced
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
fumed Si
Final Polishing Step:
1 µm diamond paste
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.87
% points with CI>0.1:
0.93
% points with CI>0.1:
0.91
% points with CI>0.1:
0.821
% points with CI>0.1:
0.7056
Alloy:
ZX30
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
95.9 %
Total Fraction Less than 1º:
65.4 %
Total Fraction Less than 1º:
88.7 %
Total Fraction Less than 1º:
32.6 %
Total Fraction Less than 1º:
96.5 %
Composition Ca content:
0.096 wt%
Number of grains:
653
Number of grains:
561
Number of grains:
473
Number of grains:
532
Number of grains:
618
Average Diameter:
18 µm
Average Diameter:
16 µm
Average Diameter:
17 µm
Files
Gleeble (1)
Settings
Test Date:
4/5/24
Testing Mode:
PSC
Initial height or thickness:
9.96 mm
Initial width:
14.99 mm
Initial length:
19.95 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.7056
% points with CI>0.1:
0.821
% points with CI>0.1:
0.91
% points with CI>0.1:
0.93
% points with CI>0.1:
0.87
Alloy:
ZX30
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
96.5 %
Total Fraction Less than 1º:
95.9 %
Total Fraction Less than 1º:
88.7 %
Total Fraction Less than 1º:
65.4 %
Total Fraction Less than 1º:
32.6 %
Composition Ca content:
0.096 wt%
Number of grains:
473
Number of grains:
561
Number of grains:
653
Number of grains:
532
Number of grains:
618
Average Diameter:
17 µm
Average Diameter:
18 µm
Average Diameter:
16 µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.87
% points with CI>0.1:
0.7056
% points with CI>0.1:
0.821
% points with CI>0.1:
0.91
% points with CI>0.1:
0.93
Alloy:
ZX30
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
95.9 %
Total Fraction Less than 1º:
32.6 %
Total Fraction Less than 1º:
88.7 %
Total Fraction Less than 1º:
96.5 %
Total Fraction Less than 1º:
65.4 %
Composition Ca content:
0.096 wt%
Number of grains:
561
Number of grains:
618
Number of grains:
532
Number of grains:
653
Number of grains:
473
Average Diameter:
18 µm
Average Diameter:
16 µm
Average Diameter:
17 µm