Sample: ZX30_TD200_TA310_0s
Ungroup ProcessesEBSD (1)
Settings
Scan date:
4/17/24
SEM view field width:
550
µm
Scan Width:
400
µm
Scan Height:
400
µm
Step size:
1
µm
frames per second:
60
fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
1 µm diamond paste
CI>0.1 after rescan:
0.752
Voltage:
30
kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.671
Alloy:
ZX30
Unloaded strain:
17%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
14.9
%
Composition Ca content:
0.096
wt%
Number of grains:
868
Average Diameter:
10
µm
Files
Gleeble (1)
Settings
Test Date:
4/5/24
Testing Mode:
PSC
Initial height or thickness:
9.97
mm
Initial width:
15.07
mm
Initial length:
20.02
mm
Final height or thickness:
8.26
mm
Final length:
21.06
mm
Pre-deformation soak Temp:
200
ºC
Deformations:
1
Initial Strain Rate:
0.5
/s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200
ºC
Post-deformation Soak Temp:
310
ºC
Post-deformation Soak Time:
0
s
Quench Duration:
45
s
Rate to Temp:
5
ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600
s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.671
Alloy:
ZX30
Unloaded strain:
17%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
14.9
%
Composition Ca content:
0.096
wt%
Number of grains:
868
Average Diameter:
10
µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1
hr
Solution treatment Temp:
325
ºC
Measurements
% points with CI>0.1:
0.671
Alloy:
ZX30
Unloaded strain:
17%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
14.9
%
Composition Ca content:
0.096
wt%
Number of grains:
868
Average Diameter:
10
µm