Sample: ZX30_TD200_TA310_128s
Ungroup ProcessesEBSD (1)
Settings
Scan date:
04/05/24
SEM view field width:
550
µm
Scan Width:
400
µm
Scan Height:
400
µm
Step size:
1
µm
frames per second:
70
fps
EBSD Camera Binning:
1 x 1
Background setting:
enhanced
Grid type:
hexagonal
Final Polishing Step:
1 µm diamond paste
Voltage:
30
kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.8
Alloy:
ZX30
Unloaded strain:
17%
Unloaded strain:
100%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
64.3
%
Composition Ca content:
0.096
wt%
Number of grains:
1103
Average Diameter:
12
µm
Files
Gleeble (2)
Settings
Test Date:
4/1/24
Testing Mode:
PSC
Initial height or thickness:
9.95
mm
Initial height or thickness:
9.96
mm
Initial width:
15.04
mm
Initial width:
15.06
mm
Initial length:
20
mm
Initial length:
19.98
mm
Pre-deformation soak Temp:
200
ºC
Final height or thickness:
8.22
mm
Final length:
21.13
mm
Deformations:
1
Initial Strain Rate:
0.5
/s
Pre-deformation soak Temp:
200
ºC
Strain Per pass:
0.2
Deformations:
1
Initial Strain Rate:
0.5
/s
Stage One - Temp during Deformations:
200
ºC
Strain Per pass:
0.2
Post-deformation Soak Temp:
310
ºC
Post-deformation Soak Time:
128
s
Stage One - Temp during Deformations:
200
ºC
Quench Duration:
45
s
Post-deformation Soak Temp:
310
ºC
Post-deformation Soak Time:
128
s
Rate to Temp:
5
ºC/s
Quench Duration:
45
s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600
s
Rate to Temp:
5
ºC/s
Program Strain Type:
TRUE
Specimen orientation:
CD || ED
Pre-deformation Soak Time:
600
s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.8
Alloy:
ZX30
Unloaded strain:
100%
Unloaded strain:
17%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
64.3
%
Composition Ca content:
0.096
wt%
Number of grains:
1103
Average Diameter:
12
µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1
hr
Solution treatment Temp:
325
ºC
Measurements
% points with CI>0.1:
0.8
Alloy:
ZX30
Unloaded strain:
100%
Unloaded strain:
17%
Composition Zn content:
3.03
wt%
Total Fraction Less than 1º:
64.3
%
Composition Ca content:
0.096
wt%
Number of grains:
1103
Average Diameter:
12
µm