Sample: ZX30_TD200_TA310_578s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78890
EBSD (3)
Settings
Scan date:
4/16/24
Scan date:
4/17/24
Scan date:
4/29/24
SEM view field width:
550 µm
Scan Width:
400 µm
Scan Height:
400 µm
Step size:
1 µm
frames per second:
124 fps
frames per second:
100 fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Background setting:
enhanced
Grid type:
hexagonal
Final Polishing Step:
1 µm diamond paste
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.88
% points with CI>0.1:
0.779
% points with CI>0.1:
0.717
Alloy:
ZX30
Unloaded strain:
18%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
46.6 %
Total Fraction Less than 1º:
89.7 %
Composition Ca content:
0.096 wt%
Number of grains:
575
Number of grains:
470
Average Diameter:
18 µm
Average Diameter:
17 µm
Files
Gleeble (1)
Settings
Test Date:
4/5/24
Testing Mode:
PSC
Initial height or thickness:
9.95 mm
Initial width:
14.97 mm
Initial length:
19.99 mm
Final height or thickness:
8.13 mm
Final length:
21.04 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
310 ºC
Post-deformation Soak Time:
578 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.88
% points with CI>0.1:
0.779
% points with CI>0.1:
0.717
Alloy:
ZX30
Unloaded strain:
18%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
46.6 %
Total Fraction Less than 1º:
89.7 %
Composition Ca content:
0.096 wt%
Number of grains:
470
Number of grains:
575
Average Diameter:
17 µm
Average Diameter:
18 µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.717
% points with CI>0.1:
0.779
% points with CI>0.1:
0.88
Alloy:
ZX30
Unloaded strain:
18%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
46.6 %
Total Fraction Less than 1º:
89.7 %
Composition Ca content:
0.096 wt%
Number of grains:
470
Number of grains:
575
Average Diameter:
18 µm
Average Diameter:
17 µm
Files