Sample: ZX30_TD200_TA350_570s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78897
EBSD (5)
Settings
Scan date:
1/12/23
Scan date:
12/27/22
Scan Width:
2000 µm
Scan Width:
1000 µm
Scan Width:
400 µm
Scan Height:
1000 µm
Scan Height:
400 µm
Step size:
5 µm
Step size:
2 µm
Step size:
1 µm
frames per second:
150 fps
EBSD Camera Binning:
1 x 1
Final Polishing Step:
1 µm diamond paste
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.915
% points with CI>0.1:
0.79
% points with CI>0.1:
0.7
% points with CI>0.1:
0.72
% points with CI>0.1:
0.71
Basal PF Max:
2.5 MRD
name on specimen mount:
ZX30_200T_600sat350_d01
Unloaded strain:
18%
Alloy:
ZX30
Total Fraction Less than 1º:
95.3 %
Total Fraction Less than 1º:
94.4 %
Composition Zn content:
3.03 wt%
Number of grains:
294
Number of grains:
1438
Average Diameter:
27 µm
Average Diameter:
23.4 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.003
Twin fraction:
0.001
Files
Gleeble (1)
Settings
Test Date:
12/16/22
Test Mode:
PSC
Testing Mode:
PSC
Initial height or thickness:
9.96 mm
Initial width:
14.93 mm
Initial length:
19.9 mm
Final height or thickness:
8.2 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
350 ºC
Post-deformation Soak Time:
570 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.79
% points with CI>0.1:
0.7
% points with CI>0.1:
0.915
% points with CI>0.1:
0.72
% points with CI>0.1:
0.71
Basal PF Max:
2.5 MRD
name on specimen mount:
ZX30_200T_600sat350_d01
Unloaded strain:
18%
Alloy:
ZX30
Total Fraction Less than 1º:
94.4 %
Total Fraction Less than 1º:
95.3 %
Composition Zn content:
3.03 wt%
Number of grains:
294
Number of grains:
1438
Average Diameter:
27 µm
Average Diameter:
23.4 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.003
Twin fraction:
0.001
Files
Optical Microscopy (1)
Settings
Date:
12/21/2022
Measurements
% points with CI>0.1:
0.915
% points with CI>0.1:
0.71
% points with CI>0.1:
0.72
% points with CI>0.1:
0.79
% points with CI>0.1:
0.7
Basal PF Max:
2.5 MRD
name on specimen mount:
ZX30_200T_600sat350_d01
Unloaded strain:
18%
Alloy:
ZX30
Total Fraction Less than 1º:
94.4 %
Total Fraction Less than 1º:
95.3 %
Composition Zn content:
3.03 wt%
Number of grains:
294
Number of grains:
1438
Average Diameter:
27 µm
Average Diameter:
23.4 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.001
Twin fraction:
0.003
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.71
% points with CI>0.1:
0.72
% points with CI>0.1:
0.7
% points with CI>0.1:
0.79
% points with CI>0.1:
0.915
Basal PF Max:
2.5 MRD
name on specimen mount:
ZX30_200T_600sat350_d01
Unloaded strain:
18%
Alloy:
ZX30
Total Fraction Less than 1º:
94.4 %
Total Fraction Less than 1º:
95.3 %
Composition Zn content:
3.03 wt%
Number of grains:
294
Number of grains:
1438
Average Diameter:
27 µm
Average Diameter:
23.4 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.001
Twin fraction:
0.003
Files
Texture (1)
Settings
total area:
6 mm^2
Measurements
% points with CI>0.1:
0.71
% points with CI>0.1:
0.915
% points with CI>0.1:
0.79
% points with CI>0.1:
0.7
% points with CI>0.1:
0.72
Basal PF Max:
2.5 MRD
name on specimen mount:
ZX30_200T_600sat350_d01
Unloaded strain:
18%
Alloy:
ZX30
Total Fraction Less than 1º:
95.3 %
Total Fraction Less than 1º:
94.4 %
Composition Zn content:
3.03 wt%
Number of grains:
294
Number of grains:
1438
Average Diameter:
23.4 µm
Average Diameter:
27 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.001
Twin fraction:
0.003
Files