Sample: Aging treatment at 168C for 50 hours Ungroup Processes
Last Updated: 4 years ago Owner: Jiashi Miao ID: 6807

The samples were solution treated at 413C for 20 hours followed by aging treatment at 168C for 50 hours.

Measurement of the length and width of Mg17Al12 precipitates after aging treatment at 168 C for 50 hours (1)
Stage:
standard
Spot Size:
No value
Scanning:
bright_field
Camera Length:
12 cm
Voltage:
No value
Apparatus:
JEOL2010F TEM
Conventional Scanning:
yes
Files
SVDC AZ91 magnesium alloy (1)
Production method:
No value
Supplier:
No value
Manufacturing Date:
No value
Manufacturer:
No value
TEM (4)
Stage:
{ "name": "Standard", "value": "standard" }
Voltage:
200000
Scanning:
{ "name": "Bright Field", "value": "bright_field" }
Mode:
{ "name": "Diffraction", "value": "diffraction" }
Conventional Scanning:
{ "name": "Yes", "value": "yes" }
Apparatus:
JOEL 2010F
Voltage:
No value
Camera Length:
No value
Scanning:
No value
Apparatus:
No value
Stage:
No value
Spot Size:
No value
Mode:
No value
Conventional Scanning:
No value