Anodic Polarization (1)

Files

• Fig. 4.tif
  

Electrochemical Quantification (1)

Files

• Fig. 10(a) anodic HER comparative.xlsx
• Fig. 10(a).tif
  
• Fig. 10(b) Current Comparison.xlsx
• Fig. 10(b).tif
  

Free Immersion (1)

Files

• Fig. 2(b).tif
  
• Fig. 3(b).tif
  

Mg-Zn-Ca-Mn receive sample (1)

Production Method:

{ "name": "Unknown", "value": "unknown" }

Supplier:

No value

Manufacturer:

nanoMag, LLC

Manufacturing Date:

No value

SEM Cross Section (2)

Specimen/Stage Bias:

No value V

Magnification:

No value

Detector:

{ "name": "Secondary", "value": "secondary" }

Voltage:

5 kV

Stage Tilt:

52 degrees

Stage:

No value

Working Distance:

4 mm

Current:

0.4 nA

Files

• Fig. 6.tif
  
• Fig. 7(b).tif
  

SEM surface (1)

Magnification:

No value

Detector:

{ "name": "Secondary", "value": "secondary" }

Current:

0.4 nA

Stage:

No value

Voltage:

5 kV

Specimen/Stage Bias:

No value V

Working Distance:

4 mm

Stage Tilt:

-3 degrees

Files

• Fig. 5(b).tif
  

STEM/EDS mapping (1)

Conventional Scanning:

No value

Mode:

{ "name": "Scanning z-contrast", "value": "scanning_z_contrast" }

Scanning:

No value

Voltage:

200 kV

Spot Size:

No value

Apparatus:

No value

Camera Length:

No value

Stage:

No value

Files

• Fig. 1(b) and (c).tif
  

TEM/STEM Cross Section (2)

Conventional Scanning:

No value

Scanning:

No value

Stage:

{ "name": "Cryo", "value": "cryo" }

Voltage:

200 kV

Apparatus:

No value

Spot Size:

No value

Mode:

No value

Camera Length:

No value

Files

• Fig. 8.tif
  
• Fig. 9.tif