Dataset: Early oxidation behavior of Si-coated titanium
Samples
7
in dataset
Process Types
13
unique activities
Avg Process Depth
3.3
processes per sample
With Processes
5
have ≥1 process
Process Participation
How many samples participated in each process
Sample Depth
How many processes each sample participated in
| Name | APT | Arc Melting of Ti5Si3 | Coating with 250 nm thick pure Si layer | Coating with 250 nm thick SiO2 layer | Obtain Titanium Material | Oxidation Exposure - 2 h | Oxidation Exposure - 32 h | Oxidation Exposure - 64 h | Oxidation Exposure - 8 h | Sectioning | SEM | STEM - EDS | TEM |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Commercially pure (99.999%) titanium plate, 3 mm thick | X | X | X | X | |||||||||
| 250 nm SiO2 coated titanium plate | |||||||||||||
| 250 nm SiO2 coated titanium plate | |||||||||||||
| 250 nm SiO2 coated titanium plate | X | X | X | X | X | ||||||||
| Sectioned titanium plate | X | ||||||||||||
| Ti5Si3 | X | X | X | X | |||||||||
| 250 nm Si coated titanium plate | X | X | X | X | X | X | X | X | X |